Porcelain & White Stoneware Clays
CLICK HERE FOR CLAY PRICING

C/6 Ox.

240 WHITE CLAY (Cone 6)

A very smooth plastic throwing body.
Shrinkage: 13% at C/6.
Absorption: 2.75%

Also available with grog: 240G WHITE CLAY W/GROG

C/6 Ox.

563 CREAMY WHITE STONEWARE (Cone 6)

Smooth vitreous stoneware body. Contains no fire clay.
Shrinkage: 14% at C/6.
Absorption: 1.0% at C/6.

C/6 Ox.

213 PORCELAIN CLAY (Cone 6)

A white body formulated for cone 6 firing. Plastic, throwable clay.
Shrinkage: 12% at C/6
Absorption: 1.7% at C/6

C/6 Ox.

551 V.P. PORCELAIN Cone 6)

Very plastic white porcelain. Good for throwing. Does not contain ball clay. Shrinkage: 13% at C/6.
Shrinkage: 13% at C/6
Absorption: .3% at C/6

C/6 Ox.

365 ENGLISH PORCELAIN (Cone 6)

Same as 257 but formulated to fire at a lower temperature.
Shrinkage: 13.5% at C/6.
Absorption: .60% at C/6

C/10 Oxidation

130 PORCELAIN CLAY (Cone 7-10)

A white firing, high temperature plastic body. Very fine white porcelain grog enhances strength and throwability.
Shrinkage: 10% at C/7, 12% at C/10.
Absorption: .75% at C/7, .5% at C/10.

C/10 Reduction

Back to top

C/10 Oxidation

257 ENGLISH PORCELAIN (Cone 8-10)

A porcelain body with a parian like quality. It is white, tight and translucent when thin. Contains no ball clay.
Shrinkage: 13% at C/8, 15% at C/10.
Absorption: 1% at C/8, .65% at C/10.

C/10 Reduction

181 WHITE STONEWARE BODY (Cone 6-10)

A very smooth white stoneware body. Contains no fire clay.
Shrinkage: 13% at C/6, 13.9% at C/10.
Absorption: 2.8% at C/6, 1.7% at C/10.

C/6 Oxidation

C/10 Oxidation

C/10 Reduction

Back to top

C/6 Oxidation

182 WHITE STONEWARE BODY (Cone 6-10)

Near white plastic stoneware body. Good for use with bright glazes. Available with and without fine grog.
Shrinkage: 10.5% at C/6, 12% at C/10.
Absorption: 5.5% at C/6, 2.1% at C/10.

C/10 Oxidation

C/10 Reduction

Woodfired

437 TROY PORCELAIN (Cone 9-13)

A versatile, plastic English kaolin body. It throws and takes glazes well, and can be used in reduction, wood, and salt firings. Translucent when thin; wide range of color/texture in long wood firings.
Shrinkage: 13% at Cone 10
Absorption: 0.3 % at Cone 10.

Sample was woodfired without glaze.

Back to top

Woodfired

508 WOODFIRE STONEWARE CLAY (C/10+)

Extremely versatile clay body for throwing and handbuilding. Fires to a very light gray color. Works well in both woodfiring and reduction.
Shrinkage: 12% at Cone 10
Absorption: 1.5% at C/10.

Sample was woodfired without glaze.

600 TURNER'S BEST PORCELAIN (Cone 6-9)

Tom Turner's porcelain is extremely white and very plastic. Excellent for throwing and very translucent. Contains no ball clay or inorganic plasticizers. #600 is completely vitreous at C/9.
Shrinkage: 12% at C/6, 15% at C/9.
Absorption: 1.4% at C/6

Woodfired

621 TROY WOODFIRE CLAY (Cone 10+)

Woodfire body formulated with Helmer kaolin. Very plastic throwing body, Excellent flashing results.
Shrinkage: 12% at Cone 10
Absorption: 0.4% at C/10
Sample was woodfired without glaze.

Certified Non-Toxic in moist form.